孕育剂
孕育剂是一种可促进石墨化，减少白口倾向，改善石墨形态和分布状况，增加共晶团数量，细化基体组织，
它在孕育处理后的短时间内（约5—8分钟）有良好的效果。主要适用于各种情况的一般然件或后期瞬时孕育。
孕育剂有硅钡钙孕育剂、硅铁粒孕育剂、硅锶孕育剂、硅锆孕育剂.
|
硅钡钙及硅铁粒含量 | ||||
|
Si |
Ba |
Ca |
Al |
Fe |
|
68-72 |
2.0-4.0 |
1.0-3.0 |
1.5 |
Balance |
|
68-74 |
2.0-3.0 |
1.5-2.0 |
1.5 |
Balance |
|
70-75 |
1.0-2.0 |
1.0-2.0 |
1.5 |
Balance |
|
65-70 |
1.0-2.0 |
1.5 |
Balance | |
|
70-72 |
1.0-2.0 |
1.5 |
Balance | |
|
72-75 |
1.0-2.0 |
1.5 |
Balance | |
|
硅锶孕育剂含量 | |||||
|
Si73Sr1.0 |
Si73-78 |
Ca≤0.1 |
Al≤0.1 |
Sr0.6-1.4 |
Fe Balance |
|
Si73Sr1.5 |
Si73-78 |
Ca≤0.1 |
Al≤0.1 |
Sr1.4-1.7 |
Fe Balance |
|
Si73Sr0.8 |
Si73-78 |
Ca≤0.1 |
Al≤0.1 |
Sr0.6-1.0 |
Fe Balance |
|
Si73Sr0.8 |
Si46-50 |
Ca≤0.1 |
Al≤0.1 |
Sr0.6-1.0 |
Fe Balance |
|
硅锆孕育剂 | ||||||
|
Zr35-45 |
Si45-50 |
Ca0.05 |
P0.04 |
S0.02 |
C0.5 |
H₂O 0.05 |
|
Zr22-27 |
Si38-43 |
Al0.5-1.0 |
C0.1-0.5 |
|||
|
Zr20-40 |
Si45-55 |
Al<0.5， |
P<0.1 |
|||
|
Zr52-54 |
Si23-27 |
Al5-7 |
Ti0.6 |
P0.88 |
C0.06-0.12 |
|
|
zr16.5-19.5 |
si2.2-3.2 |
Al21-28 |
Fe47.5-51.5 | |||
Size: 0.2-0.5mm、0.2-0.8mm、0.5-2mm、0.5-1mm、1-3mm、1-10mm、3-10mm
化学成分/粒度/包装可以根据客户要求定制生产，欢迎联系我们。